Cosmetic composition comprising a particle dispersion

ABSTRACT

Cosmetic composition comprising a particle dispersion The invention relates to a cosmetic makeup composition and/or care composition for the skin of the lips, comprising a dispersion of particles, in a cosmetically acceptable medium, the particles comprising an at least external supple phase comprising at least one supple polymer having at least one glass transition temperature of less than or equal to 60° C., and an at least internal rigid phase which is a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase. The invention also relates to the use of such a particle dispersion to improve the comfort and staying power of cosmetic compositions.

[0001] The present invention relates to a cosmetic makeup composition and/or care composition for the skin and the lips, comprising a dispersion of multiphase particles in a physiologically acceptable medium. The invention also relates to a makeup process or care process for the skin.

[0002] The use of film-forming polymers as an aqueous dispersion in cosmetic compositions, as described, for example, in EP-A-0 775 483, makes it possible to increase the staying power of the composition applied to the skin. However, while these cosmetic compositions are drying on the skin, they often give rise to sensations of tautness that the user finds unpleasant, making the composition uncomfortable to wear. These problems of comfort are especially associated with the mechanical properties of the deposits obtained on the skin. In particular, when the film formed on the skin after applying the composition is too rigid, it leaves an unpleasant mask sensation, for example during movements of the face.

[0003] In addition, the film deposited on the skin may be damaged by rubbing with the fingers or fabrics (towels, handkerchiefs or clothing) and disintegrate: in this case, the film has poor staying power, especially poor resistance to rubbing.

[0004] Moreover, a cosmetic composition comprising polymer particles dispersed in an oily medium and surface-stabilized with a stabilizer that may be a block polymer, a polymer grafted with pendent chains, or a random polymer, is known from document EP-A-0 987 012. Such a composition has transfer-resistance properties. However, the stabilizer can be dissolved in the dispersion medium during storage of the composition in the jar or during its use, giving rise to instability of the composition, which is no longer homogeneous.

[0005] Moreover, when the cosmetic composition comprises a film-forming compound that forms a particularly supple film, the composition, after application to the skin, generally forms a sticky film, making the composition unpleasant for the user to apply, especially due to the sensation of a sticky surface effect when the composition is applied to the skin.

[0006] There is thus still a need for a stable cosmetic composition to be applied to the skin and to the lips, which forms a deposit that is comfortable on the skin and the lips and that shows good staying power, especially good resistance to rubbing.

[0007] The inventors have discovered that such a composition may be obtained by using a dispersion of particular multiphase particles in a cosmetically acceptable medium.

[0008] Surprisingly, the Applicant has found that such a composition gives a deposit on the skin that shows noteworthy cosmetic properties. In particular, such a composition is comfortable to apply and shows good staying power, especially good resistance to rubbing. It has no surface stickiness and has very good mechanical qualities once applied to the skin, after drying. In addition, the composition is stable, i.e. there is no decomposition of the two rigid and supple phases of the particles, with respect to each other, thus avoiding the appearance, in the packaging or during or following the application of the composition, of macroscopic heterogeneous areas.

[0009] The advantage of such compositions is also that it has properties of absence of migration and of “transfer resistance”. The term “migration” means an overflowing of the composition beyond the initial mark. Specifically, large migration of a cosmetic composition, and in general of the liquid fatty phase that may be present in said composition, in particular when it is charged with coloring materials, leads to an unattractive effect around the area of application, for example around the lips and the eyes, which particularly accentuates wrinkles and fine lines. The composition according to the invention thus makes it possible to limit, especially in hot and humid regions, the migration of a part of the composition into the wrinkles and fine lines, after it has been deposited on the skin or the lips. Furthermore, the cosmetic composition, especially the makeup composition or care composition, according to the invention shows virtually no transfer, i.e. it virtually does not come off, leaving marks, on certain supports with which it may be placed in contact, and especially a glass, an item of clothing or the skin. Consequently, the user does not need to regularly freshen the application of the composition, especially of a foundation or lipstick, and does not have to tolerate the appearance of these unacceptable marks, for example on blouse collars.

[0010] More precisely, one subject of the invention is a cosmetic makeup composition and/or care composition for the skin and the lips, comprising a dispersion of particles in a cosmetically acceptable medium, the particles comprising at least one at least external supple phase comprising at least one supple polymer having at least one glass transition temperature of less than or equal to 60° C., and at least one at least internal rigid phase which is a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase.

[0011] The glass transition temperature corresponds to the temperature at which the amorphous material changes from a glassy solid state to a rubbery state. This temperature may be measured by differential thermal analysis (DTA) and differential calorimetry (“DSC” method, for “Differential Scanning Calorimetry”). In particular, the glass transition temperature may be measured by differential calorimetry (DSC) according to ASTM standard D3418-97.

[0012] The expression “cosmetically acceptable medium” means a medium that is compatible with keratin materials, for instance human skin.

[0013] The particles according to the invention, also known as multiphase particles (or composites), are particles comprising at least one supple phase and at least one rigid phase.

[0014] The supple polymer of the particles in dispersion has at least one glass transition temperature of less than or equal to 60° C., especially ranging from −120° C. to 60° C., preferably less than or equal to 45° C., especially ranging from −120° C. to 45° C. and preferentially less than or equal to 30° C., especially ranging from −120° C. to 30° C.

[0015] The supple polymer may be chosen from block polymers and/or random polymers. The expression “block polymers and/or random polymers” means polymers whose monomer distribution on the main chain or pendent chain members is in block and/or random form.

[0016] The supple polymer may be chosen from free-radical polymers, polycondensates and silicone polymers. The supple polymer may be chosen from polyacrylics, polymethacrylics, polyamides, polyurethanes, polyolefins, especially polyisoprenes, polybutadienes and polyisobutylenes (PIB), polyesters, polyvinyl ethers, polyvinylthio ethers, polyoxides, polysiloxanes and especially polydimethylsiloxanes (PDMS), and combinations thereof. The term “combinations” means copolymers that may be formed from monomers, leading to the formation of said polymers.

[0017] Preferably, the supple polymer may be chosen from poly(meth)acrylics, polyurethanes, polyolefins and polysiloxanes.

[0018] The rigid phase of the multiphase particles is formed from a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., especially greater than 40° C. and less than or equal to 2500° C., preferably greater than or equal to 60° C., especially ranging from 60° C. to 2500° C., and preferentially greater than or equal to 80° C., especially ranging from 80° C. to 2500° C.

[0019] For the purposes of the invention, the expression “semicrystalline material” means a material, especially a polymer, comprising a crystallizable portion and an amorphous portion having a reversible first-order temperature of change of phase, in particular of melting (solid-liquid transition).

[0020] The expression “functionalized crystalline or semicrystalline material” means a material with crystalline portions comprising reactive groups (or reactive functions) capable of forming a covalent bond with the supple polymer of the supple phase of the particles. Examples of reactive groups (reactive functions) that may be mentioned include —COOH, (acid function), —OH and —SH groups, amines (for example —NH₂) (basic function), and ethylenic double bonds (reactive double bonds).

[0021] The melting point or combustion temperature of the crystalline or semicrystalline material corresponds to the endothermic peak measured by differential thermal analysis (DTA method) or by differential calorimetry (DSC method, for “Differential Scanning Calorimetry”). The melting point or combustion temperature may be measured especially by differential calorimetry (DSC) according to ASTM standard E794-98.

[0022] The crystalline or semicrystalline material of the rigid phase may be an organic material or a mineral material.

[0023] According to a first embodiment of the invention, said crystalline or semicrystalline material may be a wax. For the purposes of the present invention, a wax is a lipophilic fatty compound that is solid at room temperature (25° C.), with a reversible solid/liquid change of state, having a melting point of greater than 45° C. and better still greater than 55° C., which may be up to 200° C., and which has an anisotropic crystal organization in the solid state.

[0024] The wax is preferably chosen from waxes containing at least one free group such as —COOH or —OH groups or an ethylenic double bond (present especially in unsaturated hydrocarbon-based chains). These reactive groups may be present in the natural form in the wax, or the wax may be modified to introduce such groups onto the wax.

[0025] The wax may be chosen from the waxes generally used in cosmetics; examples that may be mentioned include waxes of natural origin, for instance beeswax, carnauba wax, candelilla wax, ouricoury wax, Japan wax, cork fiber wax or sugarcane wax, lignite waxes, lanolin wax, montan wax and ozokerites, and also waxes of synthetic origin, for instance polyethylene waxes derived from the polymerization of ethylene, waxes obtained by Fisher-Tropsch synthesis, unsaturated fatty acid esters and glycerides that are solid at 40° C.

[0026] According to a second embodiment of the invention, the crystalline or semicrystalline material may be a crystalline polymer or semicrystalline polymer. For example, said material is chosen from polyolefins, for instance polyethylene, polyvinyls, polyvinylidenes, for instance polyvinylidene chloride or polytetrafluoroethylene, polyacrylics, polymethacrylics, polyvinyl alcohols, polyamides, for instance poly-β-alanine, polyesters, polyurethanes, polyethers, polyoxides, polysulfides and polysulfones, and combinations thereof.

[0027] According to a third embodiment of the invention, the functionalized crystalline or semicrystalline material may be a mineral compound containing reactive groups such as —OH groups or may be surface-treated with a surface agent containing reactive groups such as —OH or —NH₂ groups. For example, said crystalline or semicrystalline material is chosen from silica, titanium dioxide, alumina, talc, mica, kaolin, boron nitride, carbonates and hydroxyapatite, and mixtures thereof.

[0028] Said chemical grafting allows, by the formation of covalent bonds, stable bonding of the rigid phase and the supple phase of the multiphase particles. The chemical grafting is thus formed by covalent bonding of the rigid phase and of the supple phase of the particles.

[0029] The chemical grafting may take place by reaction of the reactive groups of the crystalline or semicrystalline material of the rigid phase with at least one monomer of the supple polymer, depending on the compatibility of the reactive group with the type of polymerization allowing the production of the supple polymer.

[0030] Thus, when the supple polymer is a polycondensate, the reactive groups of the crystalline or semicrystalline material that are compatible with polycondensation polymerization are, for example, —OH, —SH, —COOH or —NH₂ groups.

[0031] When the supple polymer is a free-radical polymer, the reactive groups of the crystalline or semicrystalline material that are compatible with free-radical polymerization are, for example, groups comprising an ethylenic unsaturation (ethylenic double bonds) or —OH groups in the form of an —OH° free-radical group.

[0032] If the crystalline or semicrystalline material does not comprise reactive groups that are compatible with the type of polymerization allowing the production of the supple polymer, it is then possible to use a grafting monomer allowing a compatible reactive group to be grafted on. The grafting monomer may be chosen from (meth)acrylic acid, glycidyl (meth)acrylate, vinylamine and allylamine.

[0033] For example, the reaction of (meth)acrylic acid with a free —OH group allows an ethylenic unsaturation to be attached to the crystalline or semicrystalline material by formation of an ester bond. Another example of a grafting monomer that may be mentioned is glycidyl (meth)acrylate, which reacts with a free —COOH group and thus attaches an ethylenic unsaturation to the crystalline or semicrystalline material by formation of an ester bond, or alternatively vinylamine or allylamine, which react with a —COOH group and thus attaches an ethylenic unsaturation to the crystalline or semicrystalline material by formation of an amide bond.

[0034] In one embodiment of the invention, the particles containing rigid and supple phases are film-forming, and may have a minimum film-forming temperature (MFFT) of less than or equal to about 30° C. (especially ranging from −120° C. to 30° C.), preferably less than or equal to about 25° C. (especially ranging from −120° C. to 25° C.); the particles containing rigid and supple phases may thus form a film at a temperature of about 30° C.

[0035] The particles containing rigid and supple phases generally have a size ranging from 1 nm to 10 μm and preferably ranging from 10 nm to 1 μm. The particle size may be measured, for example, using a Brookhaven BI-90 machine by the technique of light scattering, or with a Malvern Mastersizer 2000 granulometer, or alternatively by electron microscopy.

[0036] The supple phase may be present in the particles in a content of at least 1% by volume, relative to the total volume of the particle, preferably at least 5% by volume, preferentially at least 10% by volume and even more preferably at least 25% by volume, and up to 99.999% by volume, preferably up to 99.9% by volume, preferentially up to 99% by volume and more preferentially up to 95% by volume, and in particular ranging from 1% to 99.999% by volume, preferably ranging from 5% to 99.9% by volume, especially ranging from 10% to 99.9% by volume, preferentially ranging from 25% to 99.9% by volume and even more preferably ranging from 50% to 95% by volume, or even ranging from 50% to 90% by volume.

[0037] In any case, the rigid phase and the supple phase are incompatible, i.e. they can be distinguished using the techniques that are well known to those skilled in the art, such as, for example, electron microscopy or the measurement of several glass transitions of the particles by differential calorimetry. The multiphase particles are thus inhomogeneous particles.

[0038] The morphology of the phases within the dispersed particles may be, for example, of core-shell type, with shell portions completely surrounding the core, but also of core-shell type with a plurality of cores, or an interpenetrating network of phases. In the multiphase particles, the rigid phase is at least partly and preferably predominantly internal, and the supple phase is at least partly and preferably predominantly external.

[0039] When the crystalline or semicrystalline material is a polymer, the multiphase particles may be prepared by consecutive series of polymerization, with different types of monomers. The particles of a first family of monomers are generally prepared in a separate step, or formed in situ by polymerization. Next, or at the same time, at least one other family of other monomers are polymerized during at least one additional polymerization step. The particles thus formed have at least one at least internal structure, or core, and at least one at least external structure, or shell. The formation of a “multilayer” heterogeneous structure is thus possible. A wide variety of morphologies may flow therefrom, of the core-shell type, but also, for example, with fragmented inclusions of the rigid phase in the supple phase. According to the invention, it is essential for the structure as an at least external supple phase to be more supple than the structure as an at least internal rigid phase.

[0040] When the crystalline or semicrystalline material is a wax or a mineral material, the multiphase particles may be prepared by dispersion (for example using ultrasound) of the wax or of the mineral material in the monomers of the supple phase that are then polymerized. The preparation of such particles is described especially in the following documents: “Synthesis and characterization of novel film-forming vinyl polymer/silica colloidal nanocomposites”, J. I. Amalvy, Langmuir, vol. 17, No. 16, 2001: “Surface-initiated anionic polymerization on silica and silica surfaces”, Zhou Q., Polymer preprints, San Francisco 2000, American Chemical Society Meeting: EP 1 016 684.

[0041] The multiphase particles present in the composition according to the invention are in dispersion in a physiologically acceptable medium.

[0042] According to a first embodiment of the invention, the multiphase particles may be dispersed in an aqueous medium, especially a hydrophilic medium. The aqueous medium may consist predominantly of water, and preferably virtually totally of water. These dispersed particles thus form an aqueous polymer dispersion, generally known as a latex or pseudolatex. The term “latex” means an aqueous dispersion of polymer particles as may be obtained by emulsion polymerization of at least one monomer.

[0043] The dispersion of multiphase particles is generally prepared by at least one emulsion polymerization, in an essentially aqueous continuous phase, using reaction initiators, such as photochemical or thermal initiators for a free-radical polymerization, optionally in the presence of additives such as stabilizers, chain-transfer agents and/or catalysts.

[0044] The aqueous medium may comprise, in addition to water, a water-miscible solvent, for instance polyols, especially polyols containing from 2 to 8 carbon atoms (for example glycerol, diglycerol or ethylene glycol), C₂-C₅ lower monoalcohols (for example ethanol or isopropanol), C₂-C₄ ketones (for example acetone or diacetone), and mixtures thereof. The aqueous medium can represent from 5% to 75% by weight and better still from 5% to 50% by weight relative to the total weight of the composition.

[0045] According to a second embodiment of the invention, the multiphase particles may be dispersed in a lipophilic medium, i.e. a nonaqueous medium, especially a nonaqueous medium that is liquid at room temperature (25° C.) and atmospheric pressure.

[0046] In this case, the particles are generally prepared by at least one solution polymerization, in a solvent or organic medium, using reaction initiators, such as free-radical thermal initiators, for an essentially free-radical polymerization. The chosen solvent phase must allow the monomers to be dissolved but it must no longer be a solvent for the final polymer, which ends up in dispersion. The compounds generally present for such a preparation may be stabilizers, chain-transfer agents and/or catalysts.

[0047] The lipophilic medium may comprise a cosmetically or dermatologically acceptable oil, and more generally a physiologically acceptable oil, chosen especially from carbon-based oils, hydrocarbon-based oils, fluoro oils and/or silicone oils of mineral, animal, plant or synthetic origin, alone or as a mixture provided that they form a stable, homogeneous mixture and that they are compatible with the intended use. The oil may be a nonvolatile oil or a volatile oil, and preferably a volatile oil. The composition may also comprise a liquid fatty phase, without this phase comprising a polymer, and especially polymer particles as described above.

[0048] As oil that may be used in the invention, mention may thus be made of hydrocarbon-based oils such as liquid paraffin or liquid petroleum jelly, mink oil, turtle oil, soybean oil, perhydrosqualene, sweet almond oil, beauty-leaf oil, palm oil, grapeseed oil, sesame seed oil, corn oil, parleam oil, arara oil, rapeseed oil, sunflower oil, cottonseed oil, apricot oil, castor oil, avocado oil, jojoba oil, olive oil or cereal germ oil; esters of lanolic acid, of oleic acid, of lauric acid or of stearic acid; fatty esters, such as isopropyl myristate, isopropyl palmitate, butyl stearate, hexyl laurate, diisopropyl adipate, isononyl isononate, 2-ethylhexyl palmitate, 2-hexyldecyl laurate, 2-octyldecyl palmitate, 2-octyldodecyl myristate or lactate, 2-diethylhexyl succinate, diisostearyl malate, glyceryl triisostearate or diglyceryl triisostearate; higher fatty acids such as myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, linoleic acid, linolenic acid or isostearic acid; higher fatty alcohols such as cetanol, stearyl alcohol or oleyl alcohol, linoleyl alcohol or linolenyl alcohol, isostearyl alcohol or octyldodecanol; silicone oils such as polydimethylsiloxanes (PDMS), which are optionally phenylated such as phenyltrimethicones, or optionally substituted with aliphatic and/or aromatic groups that are optionally fluorinated, or with functional groups such as hydroxyl, thiol and/or amine groups; polysiloxanes modified with fatty acids, with fatty alcohols or with polyoxyalkylenes, fluorosilicones and perfluoro oils.

[0049] The composition according to the invention may comprise one or more oils that are volatile at room temperature. The expression “volatile oil” means any nonaqueous medium capable of evaporating from the skin or the lips or fibers, at room temperature. This volatile phase in particular comprises oils with a vapor pressure at room temperature and at atmospheric pressure ranging from 0.13 Pa to 40 000 Pa (10⁻³ to 300 mm Hg). These volatile oils especially facilitate the application of the composition to the skin. These oils may be hydrocarbon-based oils, silicone oils (optionally comprising alkyl or alkoxy groups that are pendant or at the end of a silicone chain), and fluoro oils.

[0050] As volatile silicone oil, mention may be made of linear or cyclic silicones containing from 2 to 7 silicon atoms, these silicones optionally comprising alkyl or alkoxy groups containing from 1 to 10 carbon atoms. Mention may thus be made especially of octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, hexadecamethylcyclohexasiloxane, heptamethylhexyltrisiloxane and heptamethyloctyltrisiloxane, and mixtures thereof.

[0051] Volatile hydrocarbon-based oils that may be mentioned include C₈-C₁₆ isoparaffins such as the Isopar and Permetyl products, and especially isododecane, isooctane, isodecane and isohexadecane, and mixtures thereof.

[0052] The composition may comprise represents especially from 5% to 97.5% by weight, relative to the total weight of the composition, and better still from 20% to 75% by weight, of oil and especially of volatile oil.

[0053] According to the invention, the lipophilic medium (or nonaqueous medium) described above may constitute a continuous phase of the composition or a phase dispersed in a continuous aqueous phase containing water and optionally water-soluble or water-miscible solvents such as those described above.

[0054] The multiphase particles may be present in the composition in a content ranging from 0.1% to 70% by weight of particle solids, relative to the total weight of the composition, preferably ranging from 0.5% to 55% by weight and preferentially ranging from 1% to 40% by weight.

[0055] Advantageously, the composition according to the invention is capable of forming a film that has a maximum tensile stress (for a percentage of elongation of less than 100%) of less than or equal to about 10 MPa (especially ranging from 0.1 MPa to 10 MPa) and preferably less than or equal to about 5 MPa (especially ranging from 0.1 MPa to 5 MPa). The maximum tensile stress may be determined during tensile tests as described in ASTM standard D638-99, for example on a dumbbell-shaped specimen with a working length of 33 mm and a width of 6 mm (of type IV according to the standard) at a speed of 50 mm/min. The specimens are cut into films about 100 μm thick (thickness after drying). To produce a film, the dispersions are poured into a Teflon-coated matrix, they are left to dry at a temperature equal to 25° C. in order for the volatile medium to evaporate off, and the film formed is recovered. The tests are preferentially performed on films that have been dried for at least 24 hours and better still 7 days at room temperature (25° C.) and at ambient humidity (50%).

[0056] Such a film has no surface stickiness, i.e. after contact between the finger and the surface of the film, no impression of stickiness of the surface is experienced when the contact is broken therewith by removing the finger, unlike the sensation that may be experienced after contact with an adhesive face, for example an adhesive tape.

[0057] The composition according to the invention may comprise an auxiliary film-forming agent to allow the formation of a film of the multiphase particles according to the invention at room temperature. The auxiliary agent may be a coalescer or a plasticizer known to those skilled in the art. A plasticizer is generally an organic compound that remains in the composition during the formation of the film. A coalescer is generally a volatile organic compound that evaporates off during the formation of the film.

[0058] The composition according to the invention may also comprise at least one dyestuff. The dyestuff may be chosen from the lipophilic dyes, hydrophilic dyes, pigments and nacres usually used in cosmetic or dermatological compositions, and mixtures thereof, all these compounds usually being used in cosmetic or dermatological compositions. The dyestuff is generally present in a proportion of from 0.01% to 50% by weight relative to the total weight of the composition, and preferably from 1% to 30% by weight.

[0059] The liposoluble dyes are, for example, Sudan red, D&C Red 17, D&C Green 6, β-carotene, soybean oil, Sudan brown, D&C Yellow 11, D&C Violet 2, D&C Orange 5, quinoline yellow and annatto, or mixtures thereof.

[0060] The pigments may be white or colored, mineral and/or organic, coated or uncoated, and of usual or nanometric size. The term “pigments” should be understood as meaning particles that are insoluble in the medium, intended to color and/or opacify the composition. Among the mineral pigments that may be mentioned are titanium dioxide, optionally surface-treated, zirconium oxide or cerium oxide and also iron oxide or chromium oxide, manganese violet, ultramarine blue, chromium hydrate and ferric blue, and mixtures thereof. Among the organic pigments that may be mentioned are carbon black, pigments of D&C type, and lakes based on cochineal carmine or on barium, strontium, calcium or aluminum, and mixtures thereof. The pigments may especially be coated with at least one silicone compound such as polydimethylsiloxanes and/or with polymers, especially polyetheylenes and/or at least one fluoro compound and/or at least one amino acid. Mention may also be made of “SI oxides” which are polymethylhydrogenosiloxane-coated pigments sold by the company Miyoshi.

[0061] The nacreous pigments may be chosen from white nacreous pigments such as mica coated with titanium or with bismuth oxychloride, colored nacreous pigments such as titanium mica with iron oxides, titanium mica with, especially, ferric blue or chromium oxide, titanium mica with an organic pigment of the abovementioned type, and also nacreous pigments based on bismuth oxychloride, and mixtures thereof.

[0062] The composition may also contain at least one filler, especially in order to obtain a matt product, which is especially desired for foundations and in particular for foundations or day creams for individuals with greasy skin. The term “filler” means any particle that is solid at room temperature and atmospheric pressure, used alone or in combination, which does not react chemically with the various ingredients of the composition and which are insoluble in these ingredients, even when these ingredients are brought to a temperature above room temperature and especially to their softening point or to their melting point. These inert fillers have melting points at least higher than 170° C. and better still higher than 200° C. They may be absorbent or nonabsorbent, i.e. capable in particular of absorbing the oils of the composition and also the biological substances secreted by the skin. Preferably, these fillers have an apparent diameter ranging from 0.01 to 150 μm, preferably from 0.5 to 120 μm and better still ranging from 1 to 80 μm. An apparent diameter corresponds to the diameter of the circle in which the elementary particle is inscribed along its smallest dimension (thickness for lamellae).

[0063] The fillers that may be used in the composition according to the invention may be mineral A or organic, lamellar, spherical or oblong. Mention may be made of talc, mica, silica, kaolin, polyamide powders, for instance Nylon® (Orgasol® from Atochem), poly-β-alanine powders, polyethylene powders, powders of an acrylic polymer and especially of polymethyl methacrylate (PMMA), for instance the product sold by Wackherr under the reference Covabead LH-85 (particle size 10-12 μm), powders of acrylic acid copolymers (Polytrap® from Dow Corning), polytetrafluoroethylene (Teflon®) powders, lauroyllysine, boron nitride, starch, hollow polymer microspheres such as those of polyvinylidene chloride/acrylonitrile, for instance Expancel® (Nobel Industrie), carbonates such as precipitated calcium carbonate, magnesium carbonate and magnesium hydrocarbonate, hydroxyapatite, hollow silica microspheres (Silica Beads® from Maprecos), glass microcapsules, ceramic microcapsules and polyester particles, and mixtures thereof. These fillers may be surface-treated, especially to make them lipophilic.

[0064] The composition may optionally contain one or more waxes. For the purposes of the present invention, a wax is a lipophilic fatty compound, which is solid at room temperature (25° C.) with a reversible solid/liquid change of state, having a melting point of greater than 45° C. and better still greater than 55° C., which may be up to 200° C., and having in the solid state an anisotropic crystal organization. For the purposes of the patent application, the waxes are those generally used in cosmetics and dermatology; they are especially of natural origin, for instance beeswax, carnauba wax, candelilla wax, ouricoury wax, Japan wax, cork fiber wax or sugar cane wax, paraffin wax, lignite wax, microcrystalline waxes, lanolin wax, montan wax, ozokerites and hydrogenated oils, for instance hydrogenated jojoba oil, and also of synthetic origin, for instance polyethylene waxes derived from the polymerization of ethylene, waxes obtained by Fischer-Tropsch synthesis, esters of fatty acids and of glycerides that are solid at 40° C., and silicone waxes, for instance alkyl, alkoxy, and/or esters of poly(di)methylsiloxane that are solid at 40° C. Waxes of synthetic origin are preferably used for reasons of greater reproducibility than waxes of natural origin.

[0065] The composition according to the invention also advantageously contains at least one fatty compound that is pasty at room temperature. For the purposes of the invention, the expression “pasty fatty substance” means a compound with a melting point ranging from 25 to 60° C. and preferably from 30 to 45° C. and/or a hardness ranging from 0.001 to 0.5 MPa and preferably from 0.005 to 0.4 MPa.

[0066] The melting point values correspond to the melting point measured using a differential scanning calorimeter (DSC), such as the calorimeter sold under the name DSC 2920 by the company TA Instruments, with a temperature rise of 5 or 10° C. per minute. (The melting point considered is the point corresponding to the temperature of the most endothermic peak in the thermogram).

[0067] The hardness is measured according to a method of penetration of a probe into a sample of compound and in particular using a texture analyzer (for example the TA-XT2i from Rheo) equipped with a stainless steel cylinder 2 mm in diameter. The hardness measurement is performed at 20° C. at the center of 5 samples. The cylinder is introduced into each sample at a pre-speed of 1 mm/sec and then at a measuring speed of 0.1 mm/sec, the depth of penetration being 0.3 mm. The hardness value recorded is that of the maximum peak of the applied force.

[0068] According to the invention, one or more pasty fatty substances may also be used. Preferably, these fatty substances are hydrocarbon-based compounds, optionally of polymeric type; they may also be chosen from hydrocarbon-based compounds, silicone compounds and/or fluoro compounds, and mixtures thereof.

[0069] Among the pasty compounds that may be mentioned are lanolins and lanolin derivatives, for instance acetylated lanolins or oxypropylenated lanolins, with a viscosity from 18 to 21 Pa.s and preferably 19 to 20.5 Pa.s, and/or a melting point from 30 to 45° C., and mixtures thereof. Esters of fatty acids or of fatty alcohols may also be used, especially those containing 20 to 65 carbon atoms (melting point of about 20 to 35° C. and/or viscosity at 40° C. ranging from 0.1 to 40 Pa.s), for instance triisostearyl or cetyl citrate; arachidyl propionate; polyvinyl laurate; cholesterol esters, for instance triglycerides of plant origin such as hydrogenated plant oils, viscous polyesters, for instance poly(12-hydroxystearic acid), and mixtures thereof. Triglycerides of plant origin that may be used include hydrogenated castor oil derivatives, such as “Thixinr” from Rheox.

[0070] Mention may also be made of silicone pasty fatty substances such as polydimethylsiloxanes (PDMS) containing pendant chains of the alkyl or alkoxy type containing from 8 to 24 carbon atoms, and having a melting point of 20-55° C., for instance stearyl dimethicones, especially those sold by the company Dow Corning under the trade names DC2503 and DC25514, and mixtures thereof.

[0071] The pasty fatty substance may be present in a proportion of from 0.1% to 60% by weight, relative to the total weight of the composition, preferably in a proportion of from 1% to 45% by weight and even more preferentially in a proportion of from 2% to 30% by weight, in the composition.

[0072] The composition according to the invention may contain a surfactant or a mixture of surfactants, especially a surfactant whose HLB (hydrophilic/lipophilic balance) value allows the production of a water-in-oil (W/O) or oil-in-water (O/W) emulsion.

[0073] As surfactants that may be used, suitable for obtaining a W/O emulsion, mention may be made of those with an HLB value of less than 7, and especially fatty acid esters of polyols, for instance mono-, di-, tri- or sesquioleates or stearates of sorbitol or of glycerol, glyceryl laurate or polyethylene glycol laurate; alkyl or alkoxy dimethicone copolyols with an alkyl or alkoxy chain pendant or at the end of the silicone skeleton, containing, for example, from 6 to 22 carbon atoms.

[0074] As surfactants that may be used to obtain an O/W emulsion, mention may be made of those with an HLB value of greater than 7, for instance fatty acid esters of polyethylene glycol (polyethylene glycol monostearate or monolaurate); polyoxyethylenated fatty acid esters (stearate or oleate) of sorbitol; polyoxyethylenated alkyl (lauryl, cetyl, stearyl or octyl) ethers and dimethicone copolyols; and mixtures thereof. In general, any amphoteric ionic (cationic or anionic) surfactant and any nonionic surfactant that is well known to those skilled in the art may be used.

[0075] The composition of the invention may also comprise any additive usually used in the field under consideration, chosen especially from antioxidants, essential oils, preserving agents, fragrances, neutralizers, polymers that are liposoluble or dispersible in the medium, cosmetic or dermatological active agents such as, for example, emollients, moisturizers, vitamins, essential fatty acids, sunscreens, free-radical scavengers, dispersants, for instance poly(12-hydroxystearic acid), and mixtures thereof. These additives may be present in the composition in a proportion of from 0.01% to 30% and better still from 0.01% to 10% by weight relative to the total weight of the composition. Advantageously, the composition contains at least one cosmetic or dermatological active agent.

[0076] Needless to say, a person skilled in the art will take care to select the optional additional additives and/or the amount thereof such that the advantageous properties of the composition according to the invention are not, or are not substantially, adversely affected by the envisaged addition.

[0077] According to the invention, the composition according to the invention may be in the form of a simple or multiple emulsion containing an oily or aqueous continuous phase, an oily dispersion in an aqueous phase comprising vesicles containing ionic and/or nonionic lipids, a suspension, dispersion or solution in water or an aqueous-alcoholic medium, a mousse, or a dispersion of vesicles, especially of ionic or nonionic lipids.

[0078] The composition may have the appearance of a cream, a gel, a paste, a solid (especially a stick), a solid emulsion cast in a mold in the shape of a dish, an aqueous or aqueous-alcoholic gel, a hydrophilic mousse, an emulsified gel, a two-phase or multiphase lotion, or a spray.

[0079] A person skilled in the art can select the appropriate presentation form, and also the method for preparing it, on the basis of his general knowledge, taking into account on the one hand the nature of the constituents used, especially their solubility in the support, and on the other hand the intended use of the composition.

[0080] The composition according to the invention may be a lip makeup product such as a lipstick or a lip pencil, or alternatively a lipcare product.

[0081] The composition may also be a skin makeup product (especially a colored product), for both the human face and body, in particular a foundation, optionally having care or treatment properties, a blusher, a face powder, an eye shadow, a concealer product, an eyeliner or a body makeup product, for instance temporary tattoo products. More especially, the composition according to the invention is a foundation, lipstick, eyeliner, eye shadow or face powder composition.

[0082] The composition according to the invention may also be in the form of a care composition and/or treatment composition for the skin (especially a dermatological composition), including the scalp, especially for facial and/or body skin. The skincare composition may be a skincare base, an antisun composition or a body hygiene composition, for instance deodorant products. The skincare composition may be a tinted composition.

[0083] A subject of the invention is also a cosmetic care process and/or makeup process for human skin and/or human lips comprising the application to the skin and/or the lips of a cosmetic composition as defined above.

[0084] A subject of the invention is also the use, in a cosmetic composition, of a dispersion of particles comprising an at least external supple phase comprising at least one supple polymer having at least one glass transition temperature of less than or equal to 60° C., and an at least internal rigid phase which is a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase, the particles being dispersed in a cosmetically acceptable medium, to improve the staying power and comfort of a film of the composition applied to the skin and/or to the lips.

[0085] A subject of the invention is also the use, in a cosmetic composition, of a dispersion of particles comprising an at least external supple phase comprising at least one supple polymer having a glass transition temperature of less than or equal to 60° C., and an at least internal rigid phase which is a functionalized crystalline or semicrstalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase, the particles being dispersed in a cosmetically acceptable medium, to reduce the transfer and/or deposition of marks from a film of said composition, applied to the skin and/or to the lips, onto a support placed in contact with said film.

[0086] The invention is illustrated in greater detail in the following example of a foundation. The percentages are given as mass percentages.

EXAMPLE 1

[0087] a) An aqueous dispersion of nanocomposite (multiphase particles) comprising 45% by weight of silica and grafted with an n-butyl acrylate/4-vinylpyridine copolymer (79/21 mol/mol) is prepared, in accordance with the nanocomposite described in the article “Synthesis and characterization of novel film-forming vinyl polymer/silica colloidal nanocomposites”, J. I. Amalvy, Langmuir, vol. 17, No. 16, 2001, corresponding to the reference JA26 of table 2, page 4773. A dispersion containing a particle solids content of 35% by weight is used.

[0088] b) A foundation having the composition below is prepared: aqueous nanocomposite dispersion 20% AM according to a) pigments 7% dispersant (sold under the trade name 0.02% Tamol 731DP by the company Rohm & Haas) water qs 100%

[0089] A functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., After applying the makeup to the skin, the foundation has noteworthy staying-power and transfer-resistance properties, and is comfortable for the user to wear. 

1. Cosmetic makeup composition and/or care composition for the skin and the lips comprising a dispersion of particles in a cosmetically acceptable medium, the particles comprising at least one at least external supple phase comprising at least one supple polymer having at least one glass transition temperature of less than or equal to 60° C., and at least one at least internal rigid phase which is a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase.
 2. Composition according to claim 1, characterized in that the supple polymer has a glass transition temperature ranging from −120° C. to 60° C.
 3. Composition according to claim 1 or 2, characterized in that the supple polymer has a glass transition temperature of less than or equal to 45° C.
 4. Composition according to any one of the preceding claims, characterized in that the supple polymer has a glass transition temperature ranging from −120° C. to 45° C.
 5. Composition according to any one of the preceding claims, characterized in that the supple polymer has a glass transition temperature of less than or equal to 30° C.
 6. Composition according to any one of the preceding claims, characterized in that the supple polymer has a glass transition temperature ranging from −120° C. to 30° C.
 7. Composition according to any one of the preceding claims, characterized in that the supple polymer is chosen from polyacrylics, polymethacrylics, polyamides, polyurethanes, polyolefins, polyesters, polyvinyl ethers, polyvinylthio ethers, polyoxides and polysiloxanes, and combinations thereof.
 8. Composition according to any one of the preceding claims, characterized in that the supple polymer is chosen from poly(meth)acrylics, polyurethanes, polyolefins and polysiloxanes.
 9. Composition according to any one of the preceding claims, characterized in that the functionalized crystalline or semicrystalline material of the rigid phase has a first-order phase transition, of melting or of combustion, of greater than or equal to 60° C. and preferably greater than or equal to 80° C.
 10. Composition according to any one of the preceding claims, characterized in that the functionalized crystalline or semicrystalline material has crystalline portions comprising reactive groups that are capable of forming a covalent bond with the supple polymer of the supple phase of the particles.
 11. Composition according to the preceding claim, characterized in that the reactive groups are chosen from —COOH, —OH and —SH groups, amines and ethylenic double bonds.
 12. Composition according to any one of the preceding claims, characterized in that the functionalized crystalline or semicrystalline material is a wax.
 13. Composition according to any one of claims 1 to 11, characterized in that the functionalized crystalline or semicrystalline material is a crystalline polymer or a semicrystalline polymer.
 14. Composition according to any one of the preceding claims, characterized in that the functionalized crystalline or semicrystalline material is a crystalline polymer or a semicrystalline polymer chosen from polyolefins, polyvinyls, polyvinylidenes, poly(meth)acrylics, polyvinyl alcohols, polyamides, polyesters, polyurethanes, polyethers, polyoxides, polysulfides and polysulfones, and combinations thereof.
 15. Composition according to any one of claims 1 to 11, characterized in that the functionalized crystalline or semicrystalline material is chosen from silica, titanium dioxide, alumina, talc, mica, kaolin, boron nitride, carbonates and hydroxyapatite, and mixtures thereof.
 16. Composition according to any one of the preceding claims, characterized in that the chemical grafting is formed by covalent bonding of the rigid phase and of the supple phase of the particles.
 17. Composition according to the preceding claim, characterized in that the crystalline or semicrystalline material comprises reactive groups that are capable of forming a covalent bond with the supple polymer, the chemical grafting taking place by reaction of the reactive groups of the crystalline or semicrystalline material of the rigid phase with at least one monomer of the supple polymer.
 18. Composition according to the preceding claim, characterized in that the supple polymer is a polycondensate and in that the reactive groups of the crystalline or semicrystalline material are chosen from —OH, —SH, —COOH and —NH₂ groups.
 19. Composition according to claim 17, characterized in that the supple polymer is a free-radical polymer and in that the reactive groups of the crystalline or semicrystalline material that are compatible with free-radical polymerization are chosen from groups comprising an ethylenic unsaturation or —OH groups in the form of an —OH° free-radical group.
 20. Composition according to any one of the preceding claims, characterized in that the particles containing rigid and supple phases are film-forming.
 21. Composition according to the preceding claim, characterized in that the particles have a minimum film-forming temperature of less than or equal to 30° C., preferably ranging from −120° C. to 30° C.
 22. Composition according to any one of the preceding claims, characterized in that the particles have a size ranging from 1 nm to 10 μm and preferably ranging from 10 nm to 1 μm.
 23. Composition according to any one of the preceding claims, characterized in that the supple phase is present in the particles in a content of at least 1% by volume, relative to the total volume of the particle, especially ranging from 1% to 99.999%, preferably at least 5% by volume, especially ranging from 5% to 99.9% by volume, preferentially at least 10% by volume and even more preferably at least 25% by volume, ranging from 25% to 99.9% by volume, and better still ranging from 50% to 95% by volume.
 24. Composition according to any one of the preceding claims, characterized in that the particles are dispersed in an aqueous medium.
 25. Composition according to the preceding claim, characterized in that the aqueous medium comprises water and optionally a water-miscible solvent.
 26. Composition according to the preceding claim, characterized in that the water-miscible solvent is chosen from polyols containing from 2 to 8 carbon atoms, C₂ to C₅ lower monoalcohols and C₂-C₄ ketones, and mixtures thereof.
 27. Composition according to any one of claims 24 to 26, characterized in that the aqueous medium represents from 5% to 75% by weight and better still from 5% to 50% by weight, relative to the total weight of the composition.
 28. Composition according to any one of claims 1 to 25, characterized in that the particles are dispersed in a nonaqueous medium that is liquid at room temperature and atmospheric pressure.
 29. Composition according to claim 28, characterized in that the nonaqueous medium comprises an oil.
 30. Composition according to claim 28 or 29, characterized in that the nonaqueous medium comprises a volatile oil.
 31. Composition according to the preceding claim, characterized in that the volatile oil is chosen from octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, hexadecamethylcyclohexasiloxane, heptamethylhexyltrisiloxane, heptamethyloctyltrisiloxane, isododecane, isooctane, isodecane and isohexadecane.
 32. Composition according to any one of claims 29 to 31, characterized in that the oil is present in a content ranging from 5% to 97.5% by weight and better still from 20% to 75% by weight relative to the total weight of the composition.
 33. Composition according to any one of the preceding claims, characterized in that the particles containing rigid and supple phases are present in a content ranging from 0.1% to 70% by weight of particle solids relative to the total weight of the composition, preferably ranging from 0.5% to 55% by weight and preferentially ranging from 1% to 40% by weight.
 34. Composition according to any one of the preceding claims, characterized in that the composition is capable of forming a film having a maximum tensile stress, for a percentage of elongation of less than 100%, of less than or equal to 10 MPa, preferably ranging from 0.1 MPa to 10 MPa.
 35. Composition according to the preceding claim, characterized in that the film has a maximum stress of less than or equal to 5 MPa, preferably ranging from 0.1 MPa to 5 MPa.
 36. Composition according to any one of the preceding claims, characterized in that it comprises a dyestuff.
 37. Composition according to the preceding claim, characterized in that the dyestuff is chosen from lipophilic dyes, hydrophilic dyes, pigments and nacres.
 38. Composition according to claim 36 or 37, characterized in that the dyestuff is present in a proportion of from 0.01% to 50% by weight and preferably from 1% to 30% by weight relative to the total weight of the composition.
 39. Composition according to any one of the preceding claims, characterized in that it comprises an additive chosen from plasticizers, coalescers, fillers, waxes, pasty fatty substances, surfactants, antioxidants, essential oils, preserving agents, fragrances, neutralizers, emollients, moisturizers, vitamins, essential fatty acids, sunscreens, free-radical scavengers and dispersants.
 40. Composition according to any one of the preceding claims, characterized in that it is in the form of a simple or multiple emulsion containing an oily or aqueous continuous phase, a cream, a gel, a paste, a solid, a mousse, a two-phase or multiphase lotion, or a spray.
 41. Composition according to any one of the preceding claims, characterized in that the composition is a makeup composition and/or care composition for the skin and the lips.
 42. Composition according to any one of the preceding claims, characterized in that the composition is a foundation, a blusher, a face powder, an eyeshadow, a concealer product, a lipstick, a lip gloss, a lip pencil, an eyeliner or a body makeup product.
 43. Composition according to any one of the preceding claims, characterized in that the composition is a foundation.
 44. Composition according to any one of claims 1 to 41, characterized in that the composition is in the form of a care composition and/or treatment composition for the skin and the lips, especially a skincare base, an antisun composition, a deodorant or a lipcare product.
 45. Cosmetic care process and/or makeup process for human skin and/or human lips, comprising the application to the skin and/or the lips of a cosmetic composition according to any one of the preceding claims.
 46. Use, in a cosmetic composition, of a dispersion of particles comprising an at least external supple phase comprising at least one supple polymer having at least one glass transition temperature of less than or equal to 60° C., and an at least internal rigid phase which is a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase, the particles being dispersed in a cosmetically acceptable medium, to improve the staying power and comfort of a film of the composition applied to the skin and/or the lips.
 47. Use, in a cosmetic composition, of a dispersion of particles comprising an at least external supple phase comprising at least one supple polymer having at least one glass transition temperature of less than or equal to 60° C., and an at least internal rigid phase which is a functionalized crystalline or semicrystalline material having a first-order phase transition, of melting or of combustion, of greater than 40° C., the supple polymer being at least partially attached by chemical grafting onto the rigid phase, the particles being dispersed in a cosmetically acceptable medium, to reduce the transfer and/or deposition of marks from a film of the composition, applied to the skin, onto a support placed in contact with the film. 